Tylose HS 100000 YP2

HEC
Tylose HS 100000 YP2 is a water-soluble, non-ionic, highly etherified hydroxyethyl cellulose powder. 
Tylose HS 100000 YP2 provides increased biostability, very high thickening effects and water retention, moderate foam stabilization, and high solution clarity, gloss appearance, pigment compatibility, and pseudoplasticity.
This grade Tylose HS 100000 YP2 of hydroxyethyl cellulose (HEC) is particularly well-suited for use in interior paint, non-woven fabric, and toilet cleaner / wc-gel applications.

Tylose HS 100000 YP2 is highly etherified Hydroxyethylcellulose with high biostability and retarded swelling time

Tylose HS 100000 *YP2
The meaning of "Y" in the name of Tylose HS 100000: 
*Delayed solubility
Tylose products with delayed solubility are denoted with an additional ´Y´. 
Delayed solubility Tylose grades can easily be suspended in pH neutral water without forming any lumps. 
Adjusting the pH to alkaline values can eliminate the delayed solubility. 
Please note that the pH value should be adjusted after the Tylose is completely dispersed. 
Raising the pH before dispersion results in lumps.

COMPANY
SE Tylose GmbH & Co. KG is a supplier of cellulose ethers used in the Paint & Coatings industry. 
ATAMAN CHEMICALS delivers a range of water-soluble cellulose ethers under the Tylose trade name - including methyl hydroxyethyl cellulose (MHEC), methyl hydroxypropyl cellulose (MHPC), and hydroxyethyl cellulose (HEC) - for applications such as construction and ceramic coatings & paints


Hydroxyethyl cellulose (HEC)
Tylose HEC (hydroxyethyl cellulose/Tylose H-grades) are soluble in water at any temperature. 
Tylose HEC are nonionic cellulose ethers, which are offered as free flowing powder or in granular form. 
Many Tylose HEC grades have a retarded solubility which ensures a lump free solution in aqueous systems.


Tylose HS 100000 YP2 is Hydroxyethylcellulose. 
Tylose HS 100000 YP2 by SE Tylose acts as a thickening agent. 

Hydroxyethyl cellulose. 
Tylose HS 100000 YP2 provides effects like thickening, pseudoplastic properties, water retention, protective colloid effects, film forming and a high level of salt tolerance. 
Tylose HS 100000 YP2 offers high gloss, high pigment compatibility, high pseudoplasticity, high wet scrub resistance, and very high thickening effect. 
Tylose HS 100000 YP2 exhibits moderate water retention. Tylose HS 100000 YP2 is used for paints applications like interior and exterior paints.


Tylose HS 100000 YP2 is available in powder form with delayed solubility. Tylose HS 100000 YP2 is also used in rinses, hair conditioner and hair gel.
Tylose HS 100000 YP2 Hydroxyethylcellulose  is a a non-ionic, water-soluble polymer efficient thickening agent and suspending agent.   

This brand is the Tylose HS 100000 YP2 


Application Properties of Tylose HS 100000 YP2 

The inclusion of Tylose HS 100000 YP2 can improve the following properties of dispersion paints:
• Rheological properties such as levelling and spattering
• Storage stability
• Open time
• Hiding power
• Film formation

The following properties of Tylose HS 100000 YP2 are essential for the optimisation of coating materials:
• Thickening / Adjustment of consistency
• Water retention
• Function as a protective colloid
• Binding power


Applications of of Tylose HS 100000 YP2: 
Building Materials
Paints
Oilfield
Personal Care
Home Care
Polymerisation
Ceramics
Others


Product properties 
Constitution: Hydroxyethyl cellulose
Etherification: high etherification 
Delayed solubility: yes
Particle size: powder 
Biostability: yes
Level of viscosity: 100000 mPa·s according to Höppler

Recommended fields of application in the paint:
Interior paints
Exterior paints 

Application performance of Tylose HS 100000 YP2:
Gloss: high 
Thickening effect: very high
Pigment compatibility: high 
Wet scrub resistance: high
Anti-Spattering: unfavourable 
Water retention: very high
Pseudoplasticity: high 


Typical recommended for thickening and hydration using Tylose HS 100000 YP2
Disperse Hydroxyethyl cellulose in solution, usually water, and by stir vigorously or using a blender. 
Continue to hydrate the HEC in water until completely dissolved.  
The thickening will be delayed,  this is normal and how the product is designed to work.  
(Stir until all particles are dissolved.This process allows the preparation of clear, smooth, viscous solutions in a short period of time by simply adding the R-grade to water and stirring until the polymer is completely dissolved to prevent settling of the particles.

Hydration time is  affected by several factors-  pH and temperature of the solution, and concentration level of the Tylose HS 100000 YP2 , and the presence of alkalis like TEA, Sodium hydroxide (pH) solution. 
Higher pH and higher temperatures DECREASE hydration time, but the higher pH and temperature adjustments too quickly may result in lumping. 
It's recommended that the HEC be added to room temperature water, with a neutral pH. 
Once hydrated, it can be heated and the pH can be adjusted  (typically using TEA) as needed. 
(The inhibition period, from the initial wetting to the start of dissolution,  hydration time, may vary from 5-25 min) 

Used to thicken shampoos, gels, body washes, and add body and after feel to bubble baths, body care products, lotions and creams.
Typical recommended usage levels .01% to 3%.   


Tylose HS 100000 YP2
Hydroxyethylcellulose, highly etherified, with high biostability and retarded swelling time

Product Specification
Item Specification Unit Method
Texture/Physical form powder
Solubility: soluble in water of any temperature
Ionicity: nonionic
Moisture, as packed: max. 6 % 
Ash content, as Na2SO4: max. 6 % 1140
pH-value, 1.0% solution: 5.5 - 8.0 
Particle size <0.180 mm (through 80 mesh): min. 85 % 

Viscosity Brookfield LV, 30 rpm, sp. 4 :  3800 - 5000 mPas 
1.0% dry basis, 25°C, deion. water


Thickening / Adjustment of Consistency


Technically, the most important property of Tylose HS 100000 YP2 is its capability to increase the viscosity of liquids and thus to act as a thickener. 
The thickening effect of Tylose HS 100000 YP 2 strongly depends on its concentration. 
Furthermore, the influence of the degree of polymerisation (shown in the form of different viscosity levels) on the thickening effect of Tylose can be clearly seen. 
With all other parameters constant, the viscosity of Tylose solutions increases with an increasing viscosity level.

Tylose HS 100000 YP 2 ensures the required consistency for application by providing a certain rheological profile or flow property. This makes the application of paint easy.
The amount of Tylose as well as its viscosity determines the viscosity level and leads to optimal application properties. 
During application, a decreasing viscosity with increasing shear stress is desirable. 

An important property of Tylose HS 100000 YP 2 is its pronounced water retention capability. 
Tylose HS 100000 YP 2 prevents the water from penetrating into the absorbing substrate too quickly which results in a better adhesion to the substrate. 
To the greatest possible extent, the water will be retained in the coating material during drying. 
A uniform film formation is ensured and incipient cracking is avoided.
Particularly in formulations with high pigment volume concentration, the water retaining effect of Tylose HS 100000 YP2 ensures sufficient open time for application. 
Adequate water retention in paints depends mainly on the concentration of Tylose HS 100000 YP2 and temperature of the substrate


Tylose HS 100000 YP2 functions as Protective Colloid
Coating materials are predominantly dispersions of pigments and fillers in an aqueous medium. 
Tylose HS 100000 YP2 acts as a protective colloid by preventing the agglomeration of the solid particles. 
This leads to a better storage stability and easier agitation of the paint

Especially in distempers, Tylose HS 100000 YP2 acts as a binder by combining the solid particles and binding them to the substrate. 
Tylose HS 100000 YP2 has strong adhesive power, good dry binding power and dry adhesion.
For these reasons, Tylose HS 100000 YP2 ensures a good adhesion between the coating and substrate.


Packaging, Storage, Safety instructions Packaging, Storage, Safety instructions
Like all fine-particle organic substances, cellulose ethers constitute a dust explosion hazard. 
Dust formation and deposits must be kept to a minimum so that no ignitable dust/air mixtures can form. 
Ignition sources such as naked flames, hot surfaces, sparks and static electricity should be avoided. 
Tylose HS 100000 YP2 starts to decompose at about 200°C. 
Its ignition temperature is >360°C. 
Tylose HS 100000 YP2 burns easily and the fire may spread.
When stored in closed containers, or in its original packaging in a dry place at room temperature, Tylose HS 100000 YP2 can be kept for a long time. 
In the case of high viscosity grades, a slow loss of viscosity can be measured after lengthy storage (>1 year). 
Tylose HS 100000 YP2 absorbs water from moist air. 
Once opened, container must be resealed and kept tightly closed.
This Tylose-type is supplied in multi-ply paper bags with polyethylene intermediate layer and/or in big bags.


Tylose Shinetsu HS 100000 YP2 is a white, odorless, tasteless, non-toxic, flammable and explosive powder that is often used as a thickener in methyl hydroxyethyl cellulose or hydroxyethyl cellulose grades in industry.

What is Tylose Shinetsu HS 100000 YP2 ?
Tylose is a non-ionic cellulose ether of the hydroxymethylcellulose family, which as a natural polymer has three hydroxyl groups in its structure. 
Tylose HS 100000 YP2 is usually made from raw cotton or refined pulp.

Advantages and features of Tylose Shinetsu HS 100000 YP2?
Tylose HS 100000 YP2 is a non-ionic cellulose thickener usually with the aim of enhancing viscosity, increasing concentration by means of water absorption, increasing adhesion, increasing stability, increasing degradability, increasing gloss, as a thickener for a range of organic solvents
Tylose HS 100000 YP2 is used in film formulations, emulsifiers, flow regulation, mold prevention, etc. in various formulations.

Application of Tylose HS 100000 YP2
Tylose HS 100000 YP2 is commonly used in the production of water-based resins, in the production of interior paints, in the adhesive industry, for polymerization of vinyl acetate, copolymer lactates with acrylic vinyl, in hydraulic fracture processes, in nonwovens and detergents, in Production of cosmetics, in layering of tiles, in production of paper, in production of pet bedding, for production of aqueous polymer emulsions based on ethylene-derived compounds, in production of medicine, in production of various creams and lotions, in Toothpaste production is used in the plastics industry to strengthen the viscosity of drilling fluids, etc.

Terms of use and storage of Tylose Shinetsu HS 100000?
Due to the fact that this material is flammable and its fire can spread quickly, and also its dust can explode if it is released in the environment more than expected, it is recommended to keep it in an environment that is from sources. Ignition such as flames, hot surfaces, sparks, static electricity, etc. should be away. This material also absorbs water quickly from humid air, so it is better to keep it in a closed container. This material can be stored and used for at least one year if the above points are observed.

Tylose Grades and their viscosities :
Standard Tylose H/HS
Tylose H 15 YG4 
200(mPas) (5.0 %) 
Tylose H 20 P2 
300(mPas) (5.0 %) 
Tylose H 300 NG4 
550(mPas) (2.0 %) 
Tylose H 4000 NG4 
4500(mPas) (2.0 %) 
Tylose H 10000 NG4 
7000(mPas) (2.0 %) 
Tylose H 10000 P2 
7000(mPas) (2.0 %) 
Tylose H 15000 YP2 
1200(mPas) (1.0 %) 
Tylose H 30000 YP2 
2000(mPas) (1.0 %) 
Tylose HS 30000 YP2 
2000(mPas) (1.0 %) 
Tylose H 60000 YP2 
3000(mPas) (1.0 %) 
Tylose H 100000 YP2 
4500(mPas) (1.0 %) 
Tylose HS 100000 YP2 
4500(mPas) (1.0 %) 
Cosmetic Tylose H
Tylose H 4070 NG4 
4500(mPas) (2.0 %) 
Tylose H 100070 NP2 
4500(mPas) (1.0 %) 
Special Grades Tylose MO
Tylose E 707002 4500(mPas) (2.0 %) *2 
Tylose MO 4000 P4 4500(mPas) (2.0 %) *2 

Recommended Tylose Products
▪ recommended
*1 Brookfield LV, 25 °C, deionised water
*2 Brookfield RV, 20 °C, water 20 °dH (German hardness)

Reactivity : The product is non-reactive under normal conditions of use, storage and transport.The product
is non-reactive under normal conditions of use, storage and transport
Chemical stability : Stable under normal conditions.
Possibility of hazardous reactions : No dangerous reactions known under normal conditions of use.
Conditions to avoid : No decomposition if stored normally.
Incompatible materials : Strong oxidizing agent.


Application Properties 
The inclusion of Tylose can improve the following properties of dispersion paints:
• Rheological properties such as levelling and spattering 
• Storage stability • Open time • Hiding power 
• Film formation 
The following properties of Tylose are essential for the optimisation of coating materials:
• Thickening / Adjustment of consistency
• Water retention 
• Function as a protective colloid 
• Binding power


Thickening / Adjustment of Consistency
Technically, the most important property of Tylose® is its capability to increase the viscosity of liquids and thus to act as a thickener. 
The thickening effect of Tylose strongly depends on its concentration (depicted in the diagram below). 
Furthermore, the influence of the degree of polymerisation (shown in the form of different viscosity levels) on the thickening effect of Tylose can be clearly seen. 
With all other parameters constant, the viscosity of Tylose solutions increases with an increasing viscosity level

Aqueous solutions of Tylose show a pseudoplastic effect (shear thinning), which means with an increase in shear rate, the viscosity of the solutions declines. 
This pseudoplasticity is specific to each Tylose type and the respective viscosity of the grade. 
High viscosity Tylose grades have a stronger shear thinning effect than those of low viscosity.


Thickening / Adjustment of Consistency

Tylose ensures the required consistency for application by providing a certain rheological profile or flow property. 
This makes the application of paint easy. The amount of Tylose as well as its viscosity determines the viscosity level and leads to optimal application properties. 
During application, a decreasing viscosity with increasing shear stress is desirable. 
The pseudoplasticity serves to optimise application properties of the coating system with respect to rolling, brushing resistance and spattering behaviour. 
For interior paints with low spattering the use of hydrophobic modified Tylose is recommended. 
Through the associative thickening effect with the binder, the viscosity at high shear rates will be increased, thus reducing the spatter. 
The correlation of the rheology profile of a paint and the application properties can be supplied by our technical staff.


Because of its thickening effect in coatings, Tylose acts as a stabiliser for the dispersed components. 
The formation of serum, i.e. the tendency to precipitate displayed by insoluble components such as pigments and fillers etc., is slowed down or even stopped completely. 
As a result, the coating material is protected against slow sedimentation of its components and is also stable during storage.

Water Retention
An important property of Tylose is its pronounced water retention capability. 
It prevents the water from penetrating into the absorbing substrate too quickly which results in a better adhesion to the substrate. 
To the greatest possible extent, the water will be retained in the coating material during drying. 
A uniform film formation is ensured and incipient cracking is avoided. 
Particularly in formulations with high pigment volume concentration, the water retaining effect of Tylose ensures sufficient open time for application. 
Adequate water retention in paints depends mainly on the concentration and viscosity level as well as on the type and temperature of the substrate.

Function as Protective Colloid
Coating materials are predominantly dispersions of pigments and fillers in an aqueous medium. 
Tylose acts as a protective colloid by preventing the agglomeration of the solid particles. This leads to a better storage stability and easier agitation of the paint. 
Due to its molecular structure and its specific properties, Tylose is a highly effective protective colloid. 
It is widely used in other application fields, such as polymerisation, to avoid the coagulation of the polymer.

Binding Power
Especially in distempers, Tylose acts as a binder by combining the solid particles and binding them to the substrate. 
Tylose has strong adhesive power, good dry binding power and dry adhesion. For these reasons, Tylose ensures a good adhesion between the coating and substrate.
Tylose H / HS Tylose H 6000 YP2 5200 (2.0 %) 
Tylose H 15000 YP2 1200 (1.0 %) 
Tylose H 30000 YP2 2000 (1.0 %) 
Tylose H 60000 YP2 3000 (1.0 %) 
Tylose H 100000 YP2 4500 (1.0 %) 
Tylose H 200000 YP2 5700 (1.0 %) 
Tylose HS 6000 YP2 5200 (2.0 %) 
Tylose HS 15000 YP2 1200 (1.0 %) 
Tylose HS 30000 YP2 2000 (1.0 %) 
Tylose HS 60000 YP2 3000 (1.0 %) 
Tylose HS 100000 YP2 4500 (1.0 %) 
Hydrophobically modified HEC 
Tylose HX 6000 YG4 Plus 550 (1.0 %) 
Tylose MH Tylose MH 2000 YP2 2700 (1.9 %) 
Tylose MH 6000 YP4 6700 (1.9 %) 
Tylose MH 15000 YP4 13000 (1.9 %) 
Tylose MH 30000 YP4 23000 (1.9 %) 
Special grades Tylose MB 60000 P2 31000 (1.9 %) 
Tylose PSO 810001 6300 (1.0 %)


Tylose for Personal Care

Personal Care products include all areas of nurturing and decorative cosmetics. 
Nurturing cosmetics include hair care, skin care and oral hygiene. 
Decorative cosmetics include make-up, powders, eye shadow and mascara.
In addition to the thickening effect, Tylose improves the foam stability of shaving foams, preserves moisture during a perm treatment, increases the stickiness of adhesive creams, acts as a binder in powder make-ups, and eases the distribution of colouring agents in hair. 
Being a physiologically harmless cosmetic additive, Tylose offers a multitude of applications in the field of personal care. 
Tylose hydroxyethyl cellulose (HEC) is our most widely used additive in the cosmetic field. Besides the ultra pure cosmetic types, our standard Tylose types can also be used.

Application Properties 
The following INCI designations apply to Tylose grades, which can also be seen in the International Cosmetic Ingredient Dictionary and International Buyers’ Guide. 
Hydroxyethylcellulose (HEC) (Tylose H and HS types) 
Hydroxypropyl Methylcellulose (HPMC) (Tylose MO, MOB, MOBS and MOBT types) 
Methyl Hydroxyethylcellulose (MHEC) (Tylose MH, MHB, MHS and MHBS types) 
For Personal Care the following properties of Tylose are particularly significant: 
• Thickening/Adjustment of consistency 
• Stabilisation 
• High compatibility with other raw materials such as surfactants


Application Performance
Building Materials
Consistency development: moderate
Final consistency: very low
Sag resistance:    very low
Water demand: very low
Water retention: very low
Influence on cement hydration: high
Heat stability:    very high
Personal And Home Care
Thickening effect: very low
Higher purity:    no
Clarity of the solution: high
Stabilization of foam: moderate
Pseudoplasticity: very low
Compatibility with salts: high
Compatibility with surfactants:    high


Hydroxyethylcellulose
Agent Name
Hydroxyethylcellulose

CAS Number
9004-62-0

Major Category
Other Classes

Synonyms
H. E. Cellulose; 2-Hydroxyethyl cellulose; 2-Hydroxyethyl cellulose ether; AH 15; AW 15 (Polysaccharide); BL 15; Cellosize; Cellosize 4400H16; Cellosize QP; Cellosize QP 1500; Cellosize QP 30000; Cellosize QP 4400; Cellosize QP3; Cellosize UT 40; Cellosize WP; Cellosize WP 09; Cellosize WP 300; Cellosize WP 300H; Cellosize WP 400H; Cellosize WP 4400; Cellosize WPO 9H17; Cellulose 2-hydroxyethyl ether; Cellulose hydroxyethyl ether; Cellulose hydroxyethylate; Cellulose, 2-hydroxyethyl ether; Cellulose, ethylene oxide-grafted; Cellulosize; Fuji HEC-BL 20; Glutofix 600; HEC; HEC-Al 5000; Hercules N 100; Hespan; Hetastarch; Hydroxyethyl cellulose; Hydroxyethyl cellulose ether; Hydroxyethyl ether cellulose; J 164; Natrosol; Natrosol 150L; Natrosol 180HH; Natrosol 180L; Natrosol 240JR; Natrosol 250; Natrosol 250 HHR; Natrosol 250G; Natrosol 250H; Natrosol 250H4R; Natrosol 250HHP; Natrosol 250HHR; Natrosol 250HR; Natrosol 250HX; Natrosol 250L; Natrosol 250M; Natrosol 250MH; Natrosol 300H; Natrosol LR; OETs; Oxirane, polymer with cellulose; Tylose H 20; Tylose H 300; Tylose H series; Tylose P; Tylose P-X; Tylose P-Z series; Tylose PS-X; Unicel QP 100MH; Unicel QP 300 H; Unicel QP 52000 H; Walocel HT 6.000 PFV; [ChemIDplus]

Category
Other Organic Compounds

Description
White solid; [Merck Index] Beige powder; [MSDSonline]

Sources/Uses
A starch derivative with unknown exact composition; [Merck Index] Used as a suspending agent (emulsions, jellies, ointments, lotions, suppositories, and tablets), a thickener (latex paints and paint removers), a sizing agent (paper and textiles), a colloid (polymers and textile dyes), a water-retaining agent (cements, mortars, and concrete), and a binder (ceramic glazes, films, and sheeting); Also used for secondary petroleum recovery and in medicine (artificial tear solutions, cryoprotective agent for erythrocytes, and plasma volume expander); [HSDB]

Comments
Emergency treatment: Non-toxic ingestion; [HSDB] May cause irritation; [ICSC] May cause irritation; [MSDSonline]
Biomedical References

Search PubMed
Diseases, Processes, and Activities Linked to This Agent

Processes
Industrial Processes with risk of exposure:

Cement Producing
Painting (Pigments, Binders, and Biocides)
Petroleum Production and Refining
Pulp and Paper Processing
Textiles (Fiber & Fabric Manufacturing)
Textiles (Printing, Dyeing, or Finishing)
Activities
Activities with risk of exposure:

Ceramics making

Tylose MC- and Tylose HEC-types are water-soluble cellulose ethers, produced from cellulose. Cellulose ethers are manly used as thickeners, binders, water retaining agents and dispersing agents. 
SE Tylose GmbH & Co. KG supplies more than 200 different Tylose products for many applications, whose end products can be found in almost all areas of every day life. 
The most important fields of application for Tylose are as additives for building and coating materials. 
In building materials, for example, Tylose enables the use of machine applied plasters and guarantees a highly efficient application on ceilings and walls. 
Tylose prevents the sedimentation of coatings and allows an even, almost spatter-free application of the paint.


Special applications for example: - Polymerization - Pharmaceuticals - Ceramics - Cosmetics – Cleaners


SE Tylose GmbH & Co. KG is a German subsidiary of the Shin-Etsu-Group, which is based in Japan. 
SE Tylose GmbH & Co. KG develops, produces, and sells water-soluble cellulose ethers under the tradename Tylose. 
The SE Tylose GmbH & Co. KG headquarters are in Wiesbaden (Germany) at the Industriepark KalleAlbert

SE Tylose GmbH & Co. KG employs approximately 500 people in Wiesbaden. A wide range of training possiblities guarantees their high level of qualification. 
Additionally, SE Tylose has a continuous trainee program for all departments of the company, ensuring that we are introducing and developing employees


At SE Tylose GmbH & Co. KG sites, the renewable raw material cellulose is transformed into different watersoluble cellulose ethers (Tylose MC- and HEC-types) in state of the art production plants. 
More than two thirds of the roughly 500 Shin-Etsu employees at the Industriepark Kalle-Albert work in production. 
With its capacities in Germany and Japan, the Shin-Etsu-Group is one of the biggest suppliers of methyl cellulose world-wide.


SE Tylose GmbH & Co. KG is one of the major manufacturers of cellulose ethers world wide, supplied under the brand name Tylose. 
Tylose is used in a wide variety of products and applications.

Construction materials are optimised with the following properties of Tylose:
• Water retention 
• Stabilising of air pores
• Consistency control 
• Improvement of workability
• Adhesion improvement


Cementitious thin bed adhesives are used to adhere ceramic tiles, to build walls of aerated concrete or lime stone bricks and to install exterior insulating finishing systems (EIFS). 
They offer an easy and light workability, a high efficiency and guarantee a long durability.


Cement tile adhesives have to be easy to trowel. They must provide long embedding time, high slip resistance and sufficient adhesion strength. 
These properties can be influenced by Tylose MC. 
Adhesives for block laying are used to build up walls of aerated concrete blocks, sand-lime bricks or standard bricks. 
EIFS adhesives ensure an excellent bond between substrate and insulating boards. 
Tylose MC improves the workability of EIFS adhesives and increases both adhesion and sag resistance.

Cement based Renders and Trowelling Compounds
Renders are mixtures of mineral binders, aggregates and auxiliaries. 
Depending on the process, there is a distinction between hand and machine application. 
Renders are used for base coating, insulation, renovation and decorative purposes. 
Renders based on cement or cement/hydrated lime can be employed for exterior and interior work. 
Cement based jointing and trowelling compounds are used for repairing systems and to smooth coarse walls and floors. 
Grouts are applied to fill the gaps between ceramic or stone tiles.


Tylose MC is an important additive ensuring there is sufficient water retention in renders and trowelling compounds. 
Additional advantages are better workability and an increase of the adhesion strength. 
Machine applied renders are mixed in continuously or discontinuously working plastering machines. 
These enable coverage of large wall and ceiling areas by a highly efficient technique. 
Continuously operating plastering machines need to be fed with premixed renders containing Tylose. 
Other additives (e.g. Hostapur OSB, Tylovis SE 7 or Tylovis EP 28) can be added as required.

Tylose MH 300 P2 
Tylose MH 6000 YP4 
Tylose MH 6002 P4 
Tylose MH 10007 P4 
Tylose MHS 10012 P6 
Tylose MH 15002 P6 
Tylose MB 15009 P2 
Tylose MH 20009 P2 
Tylose MHS 30027 P6 
Tylose MHS 60000 YP4 
Tylose MH 60001 P4 
Tylose MH 60001 P6 
Tylose MH 60010 P4 
Tylose MO 60016 P4 
Tylose MH 100001 P6 
Tylose H 20 P2 
Tylose H 300 P2 
Tylose HS 30000 YP2

Thickening/Adjustment of Consistency 
Tylose can thicken and adjust the consistency of hair conditioners, hair gels, toothpastes and lotions


The thickening effect of Tylose grades is dependent on the degree of polymerisation (DP) or the molecular weight and the concentration used. 
When using the same concentration, the viscosity of the solution increases with an increased degree of polymerisation. 
An increase in Tylose concentration gives a strong increase in viscosity

Aqueous solutions of Tylose grades are shear thinning liquids. 
The viscosity is decreased by an increase in shear stress, and returns to its initial viscosity when the shear stress is removed. 
High viscosity Tylose grades have a stronger shear thinning effect than those of low viscosity, which is shown in the diagram below. 
The rheological profile varies depending on the Tylose type used, e.g. Tylose H or Tylose MO

Stabilisation

Emulsions are commonly used in the field of skin care. 
A finely distributed mixture of oil and water, two liquids which are normally immiscible, exists in an emulsion without any visible segregation. 
One liquid exists as little droplets distributed within the other liquid. 
Either water in oil emulsion (W/O emulsion) or oil in water emulsion (O/W emulsion) is possible depending on which phase the droplets are formed in. 
The preferred stabilisers for O/W emulsions are thickeners that act in the water phase. 
The surface activity of Tylose is low compared to tenside products. 
However, due to its thickening effect and colloidal protective properties, Tylose offers an important contribution to the stabilisation of the emulsion formed. 
The use of low to medium viscosity Tylose H types are preferable in this case.


High Compatibility

Non-ionic Tylose H, MH, and MO types exhibit a good compatibility with numerous tensides. 
Furthermore, they are also compatible with many other raw materials such as starch, dextrin, gelatine, sorbitol and propylene glycol. 
Due to their chemical structure, Tylose grades exhibit good compatibility with electrolytes. 
Soluble phosphate, carbonate and sulphate exhibit a stronger flocculating effect in higher concentrations than nitrate and chloride. 
The electrolyte compatibility of Tylose H grades with chlorides is generally higher than that of Tylose MO grades. 
In addition AlCl3 gives a higher thickening effect with Tylose H grades (see diagram below).

Although Tylose is insoluble in most organic solvents, it exhibits relatively good solubility in water/organic solvent mixtures, such as water with ethanol, isopropanol or glycerol, even when relatively high fractions of the organic solvent are present. 
The following diagrams show the development of viscosity in water with ethanol, isopropanol and glycerol using Tylose H or MO grades.

Standard 
Tylose H/HS Tylose H 15 YG4
200 (mPas ) (5.0 %) 
Tylose H 20 P2 
300 (mPas)  (5.0 %) 
Tylose H 300 NG4 
550 (mPas )  (2.0 %) 
Tylose H 4000 NG4
4500 (mPas ) (2.0 %) 
Tylose H 10000 NG4
7000 (mPas )  (2.0 %)
Tylose H 10000 P2 
7000 (mPas ) (2.0 %) 
Tylose H 15000 YP2 
1200 (mPas ) (1.0 %) 
Tylose H 30000 YP2 
2000 (mPas )  (1.0 %) 
Tylose HS 30000 YP2 
2000 (mPas )  (1.0 %) 
Tylose H 60000 YP2 
3000 (mPas )  (1.0 %) 
Tylose H 100000 YP2
 4500 (mPas ) (1.0 %) 
Tylose HS 100000 YP2 
4500 (mPas ) (1.0 %) 
Cosmetic Tylose H Tylose H 4070 NG4 
4500 (mPas )  (2.0 %) 
Tylose H 100070 NP2 
4500 (mPas )  (1.0 %) 
Special Grades Tylose MO Tylose E 707002 
4500 (mPas )  (2.0 %) 
Tylose MO 4000 P4 
4500(mPas )  (2.0 %) *2


This information is based on our present state of knowledge and is intended to provide general notes on our products and their uses. 
It should not therefore be construed as guaranteeing specific properties of the products described or their suitability for a particular application. 
Any existing industrial property rights must be observed. 
The quality of our products is guaranteed under our General Conditions of Sale
 

Bu internet sitesinde sizlere daha iyi hizmet sunulabilmesi için çerezler kullanılmaktadır. Çerezler hakkında detaylı bilgi almak için Kişisel Verilerin Korunması Kanunu mevzuat metnini inceleyebilirsiniz.